Polypropylene details

Homopolymer PP unfilled details

Property

Description

V500X1

High crystalline

V550

General purpose

Homopolymer PP unfilled test results

Property

Test Method

V500X1

V550

Description

High crystalline

General purpose

Processing Method

Injection

Injection

Specific gravity, g/cc

ASTM D792

0.905

0.905

Linear mold shrinkage, in/in(m)

ASTM D955

.012(.012)

.013(.013)

Hardness, Rock well

ASTM D785

R100

R98

Reinforcement content %

ASTM D2584

-

-

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

1.0

(53.4)

0.8

(42.7)

Tensile strength

ASTM D638

5,300

(36.6)

4,900

(33.8)

Elongation, Ultimate %

ASTM D638

12

12

Flexural modulus

psi (MPa)

ASTM D790

240,000

(1655)

220,000

(1517)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

260(127)

170(77)

210(99)

135(57)

Special Features

High stiffness/Fast cycle

-

Homopolymer PP Calcium filled details

Property

Description

V500CC20

20% Caco3 filled homopolymer

V500CC30

30% Caco3 filled homopolymer

V500CC40

40% Caco3 filled homopolymer

Homopolymer PP Calcium test results

Property

Test Method

V500CC20

V500CC30

V500CC40

Description

20% Caco3 filled homopolymer

30% Caco3 filled homopolymer

40% Caco3 filled homopolymer

Processing Method

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

1.05

1.13

1.24

Linear mold shrinkage, in/in(m)

ASTM D955

.012(.012)

.012(.012)

.010(.010)

Hardness, Rock well

ASTM D785

R92

R82

R80

Reinforcement content %

ASTM D2584

20

30

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

0.9

(48.1 )

0.9

(48.1)

0.7

(37.4)

Tensile strength

ASTM D638

4,000

(27.6)

3,800

(26.2)

3,800

(26.2)

Elongation, Ultimate %

ASTM D638

-

-

-

Flexural modulus

psi (MPa)

ASTM D790

250,000

(1724)

300,000

(2069)

320,000

(2207)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

215(102)

140(60)

215(102)

160(71)

225(107)

160(71)

Special Features

Good surface appearance

Good surface appearance

Good surface appearance

Homopolymer PP glass fiber filled details

PropertyDescription
V500/10 10% Glass Fiber Reinforced
V500/13 13% Glass Fiber Reinforced
V500/20 20% Glass Fiber Reinforced
V500/25 25% Glass Fiber Reinforced
V500/30 30% Glass Fiber Reinforced
V500/40 40% Glass Fiber Reinforced

Homopolymer PP glass fiber test results

Property

Test Method

V500/10

V500/13

V500/20

V500/25

V500/30

V500/40

Description

10% Glass fiber reinforced

13% Glass fiber reinforced

20% Glass fiber reinforced

25% Glass fiber reinforced

30% Glass fiber reinforced

40% Glass fiber reinforced

Processing Method

Injection

Injection

Injection

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

0.97

0.99

1.04

1.08

1.13

1.23

Linear mold shrinkage, in/in(m)

ASTM D955

.008(.008)

.007(.007)

.004(.004)

.003(.003)

.003(.003)

.003(.003)

Hardness, Rock well

ASTM D785

R92

R92

R94

R94

R94

R100

Reinforcement content %

ASTM D2584

10

13

20

25

30

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

0.9

(481)

1.0

(53.4)

1.0

(53.4)

1.0

(53.4)

1.0

(53.4)

1.3

(69.4)

Tensile strength

ASTM D638

6,000

(41.4)

6,500

(44.8)

7,000

(48.3)

7,500

(51.7)

8,000

(55.2)

11,000

(75.9)

Elongation, Ultimate %

ASTM D638

4

3

3

3

3

2

Flexural modulus

psi (MPa)

ASTM D790

300,000

(2069)

410,000

(2828)

500,000

(3448)

550,000

(3793)

650,000

(4483)

800,000

(5517)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

275(135)

235(113)

270(132)

240(116)

280(138)

245(118)

290(143)

265(129)

295(146)

275(135)

300(149)

270(132)

Special Features

-

Improved impact resistance

-

Good heat resistance

Excellent heat resistance

Excellent heat resistance

Homopolymer PP Mica filled details

PropertyDescription
V500MI12 12% Mica Reinforced
V500MI15 15% Mica Reinforced
V500MI20 20% Mica Reinforced
V500MI30 30% Mica Reinforced
V500MI40 40% Mica Reinforced

Homopolymer PP Mica test results

Property

Test Method

V500MI12

V500MI14

V500MI20

V500MI30

V500MI40

Description

12% Mica reinforced

14% Mica reinforced

20% Mica reinforced

30% Mica reinforced

40% Mica reinforced

Processing Method

Injection

Injection

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

1.00

1.01

1.05

1.13

1.24

Linear mold shrinkage, in/in(m)

ASTM D955

.010(.010)

.010(.010)

.009(.009)

.008(.008)

.006(.006)

Hardness, Rock well

ASTM D785

R90

R90

R95

R95

R100

Reinforcement content %

ASTM D2584

12

15

20

30

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

0.9

(48.1)

1.0

(53.4)

1.0

(53.4)

0.7

(37.4)

0.7

(37.4)

Tensile strength

ASTM D638

4,500

(31)

4,500

(31)

4,500

(31)

4,500

(31)

11,000

(75.9)

Elongation, Ultimate %

ASTM D638

10

10

10

5

3

Flexural modulus

psi (MPa)

ASTM D790

280,000

(1931)

300,000

(2069)

330,000

(2276)

660,000

(4552)

600,000

(4138)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

210(99)

160(71)

215(102)

165(74)

230(110)

190(88)

270(132)

200(193)

275(135)

200(93)

Special Features

Excellent dimensional stability

Excellent dimensional stability

Excellent dimensional stability

High stiffness

High stiffness

Homopolymer PP Combination filled details

PropertyDescription

V500R32

32% Glass/Mineral Reinforced

V500R35

35% Glass/Mineral Reinforced

V500R40

40% Glass/Mineral Reinforced

Homopolymer PP Combination test results

Property

Test Method

V500R32

V500R35

V500R40

Description

32% Glass/Mineral reinforced

35% Glass/Mineral reinforced

40% Glass/Mineral reinforced

Processing Method

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

1.14

1.18

1.24

Linear mold shrinkage, in/in(m)

ASTM D955

.004(.004)

.004(.004)

.003(.003)

Hardness, Rock well

ASTM D785

R90

R92

R95

Reinforcement content %

ASTM D2584

32

35

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

12

(64.1)

1.0

(53.4)

1.0

(53.4)

Tensile strength

ASTM D638

8,000

(55.2)

8,800

(60.7)

9,200

(63.4)

Elongation, Ultimate %

ASTM D638

3

3

3

Flexural modulus

psi (MPa)

ASTM D790

700,000

(4828)

830,000

(5724)

850,000

(5862)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

285(141)

255(124)

290(143)

260(127)

295(146)

265(129)

Special Features

Excellent stiffness &

Dimensional stability

Excellent stiffness &

Dimensional stability

Excellent stiffness &

Dimensional stability

Homopolymer PP Talc filled details

Property Description
V500TL10 10% Talc Reinforced
V500TL20 20% Talc Reinforced
V500TL30 30% Talc Reinforced
E500TL40 40% Talc Reinforced
V500TL40 40% Talc Reinforced

Homopolymer PP Talc test results

Property

Test Method

V500TL10

V500TL20

V500TL30

E500TL40

V500TL40

Description

10% Talc reinforced

20% Talc reinforced

30% Talc reinforced

40% Talc reinforced

40% Talc reinforced

Processing Method

Injection

Injection

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

0.98

1.05

1.13

1.24

1.24

Linear mold shrinkage, in/in(m)

ASTM D955

.012(.012)

.011(.011)

.010(.010)

.009(.009)

.009(.009)

Hardness, Rock well

ASTM D785

R90

R92

R93

R95

R95

Reinforcement content %

ASTM D2584

10

20

30

40

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

0.9

(48.1)

0.8

(42.7)

0.8

(42.7)

1.2

(64.1)

0.7

(37.4)

Tensile strength

ASTM D638

5000

(34.5)

4,900

(33.8)

4,700

(32.4)

4,000

(27.6)

4,500

(31.0)

Elongation, Ultimate %

ASTM D638

25

10

10

12

10

Flexural modulus

psi (MPa)

ASTM D790

270,000

(1862)

320,000

(2207)

350,000

(2414)

330,000

(2276)

450,000

(3103)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

245(118)

145(63)

250(121)

165(74)

260(127)

170(77)

270(132)

175(79)

275(135)

175(79)

Special Features

Good dimensional stability

Good dimensional stability UL9HB

Good dimensional stability

Good dimensional stability UL9HB

Good dimensional stability UL9HB

Copolymer PP unfilled details

Property

Description

V51X1

High crystalline

V525

Block copolymer

E535

Block copolymer

V535

Block copolymer

V545

Block copolymer

Copolymer PP unfilled test results

Property

Test Method

V515X1

V525

E535

V535

V545

Description

High crystalline

Block copolymer

Block copolymer

Block copolymer

Block copolymer

Processing Method

Injection

Injection

Injection

Extr./Blow

Injection

Specific gravity, g/cc

ASTM D792

0.905

0.905

0.905

0.905

0.905

Linear mold shrinkage, in/in(m)

ASTM D955

.012(.012)

.013(.013)

.014(.014)

.014(.014)

.014(.014)

Hardness, Rock well

ASTM D785

R90

R98

R80

R80

R75

Reinforcement content %

ASTM D2584

-

-

-

-

-

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

1.5

(80.1)

0.8

(42.7)

2.5

(133)

10.0

(534)

6.0

(320)

Tensile strength

ASTM D638

4,100

(28.3)

4,900

(33.8)

3,625

(25)

4,000

(26.6)

3,100

(21.4)

Elongation, Ultimate %

ASTM D638

12

12

12

15

12

Flexural modulus

psi (MPa)

ASTM D790

200,000

(1379)

220,000

(1517)

140,000

(966)

170,000

(1172)

125,000

(862)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

255(107)

140(60)

210(99)

135(57)

185(85)

132(55)

185(85)

125(52)

182(83)

130(54)

Special Features

High stiffness/Fast cycle

-

Good balance of properties

Excellent toughness impact

Excellent low term toughness

Copolymer PP Calcium filled details

Property

Description

V525CC10

10% caco3 filled copolymer

V525CC20

20% caco3 filled copolymer

V525CC30

30% Caco3 filled copolymer

V525CC40

40% Caco3 filled copolymer

V535CC20

20% Caco3 filled copolymer

E535CC30

40% Caco3 filled copolymer

E535CC40

40% Caco3 filled copolymer

Copolymer PP Calcium test results

Property

Test Method

V525CC10

V525CC20

V525CC30

V525CC40

V535CC20

E535CC30

E535CC40

Description

10% caco3 filled copolymer

20% caco3 filled copolymer

30% caco3 filled copolymer

40% caco3 filled copolymer

20% caco3 filled copolymer

30% caco3 filled copolymer

40% caco3 filled copolymer

Processing Method

Injection

Injection

Injection

Injection

Injection

Extr./Blow

Extr./Blow

Specific gravity, g/cc

ASTM D792

0.98

1.05

1.13

1.24

1.5

1.13

1.24

Linear mold shrinkage, in/in(m)

ASTM D955

.014(.014)

.012(.012)

.012(.012)

.010(.010)

.012(.012)

.012(.012)

.010(.010)

Hardness, Rock well

ASTM D785

R70

R75

R75

R80

R75

R80

R80

Reinforcement content %

ASTM D2584

10

20

30

40

20

30

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

2.4

(128)

2.0

(107)

1.7

(90.8)

1.5

(80.1)

1.7

(90.8)

7.0

(374)

7.0

(374)

Tensile strength

ASTM D638

3,400

(234)

3,500

(24.1)

3,000

(20.7)

2,800

(19.3)

3,000

(20.7)

3,800

(26.2)

3,100

(21.4)

Elongation, Ultimate %

ASTM D638

-

-

-

-

-

-

-

Flexural modulus

psi (MPa)

ASTM D790

160,000

(1103)

210,000

(1448)

180,000

(1241)

230,000

(1586)

130,000

(897)

220,000

(1517)

220,000

(1517)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

185(85)

130(54)

190(88)

130(54)

195(91)

135(57)

215(102)

140(60)

180(82)

125(52)

215(102)

140(60)

215(102)

140(60)

Special Features

Good balance of properties

Good balance of properties

Good balance of properties

Good balance of properties

Good low temperature impact

Excellent toughness

Excellent toughness

Copolymer PP glass fiber filled details

PropertyDescription

E510/20

20% Glass Fiber Reinforced

V525/10

10% Glass Fiber Reinforced

V525/20

 20% Glass Fiber Reinforced

V525/30

30% Glass Fiber Reinforced

V525/40

40% Glass Fiber Reinforced

Copolymer PP glass fiber test results

Property

Test Method

E510/20

V525/10

V525/20

V525/30

V525/40

Description

20% Glass fiber reinforced

10% Glass fiber reinforced

20% Glass fiber reinforced

30% Glass fiber reinforced

40% Glass fiber reinforced

Processing Method

Extrusion

Injection

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

1.04

0.97

1.04

1.13

1.23

Linear mold shrinkage, in/in(m)

ASTM D955

.004(.004)

.007(.007)

.005(.004)

.003(.003)

.003(.003)

Hardness, Rock well

ASTM D785

R90

R85

R85

R90

R100

Reinforcement content %

ASTM D2584

20

10

20

30

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

2.0

(107)

1.6

(85.4)

1.6

(85.4)

2.0

(107)

1.5

(80.1)

Tensile strength

ASTM D638

6,800

(46.9)

5000

(34.5)

5,500

(37.9)

6,000

(41.4)

8,800

(60.7)

Elongation, Ultimate %

ASTM D638

3

10

5

3

3

Flexural modulus

psi (MPa)

ASTM D790

500,000

(3448)

220,000

(1517)

280,000

(1931)

610,000

(4207)

700,000

(4828)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

280(138)

255(124)

220(104)

160(71)

260(127)

210(99)

290(143)

250(121)

285(141)

260(7)

Special Features

Good balance of properties

Good impact resistance

Good impact resistance

Good impact resistance

Good impact resistance

Copolymer PP Mica filled details

PropertyDescription

V515MI12

 12% Mica Reinforced

V515MI20

20% Mica Reinforced

V525MI12

12% Mica Reinforced

V525MI25

25% Mica Reinforced

V525MI40

 40% Mica Reinforced

V526MI20

20% Mica Reinforced

V526MI25

25% Mica Reinforced

V545MI35

35% Mica Reinforced

Copolymer PP Mica test results

Property

Test Method

V515MI12

V515MI20

V525MI12

V525MI25

V525MI40

V526MI20

V526MI25

V526MI35

Description

12% Mica reinforced

20% Mica reinforced

12% Mica reinforced

25% Mica reinforced

40% Mica reinforced

20% Mica reinforced

25% Mica reinforced

35% Mica reinforced

Processing Method

Injection

Injection

Injection

Injection

Injection

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

1.00

1.05

1.00

1.28

1.24

1.05

1.08

1.21

Linear mold shrinkage, in/in(m)

ASTM D955

.011(.011)

.010(.010)

.010(.010)

.010(.010)

.006(.006)

.010(.010)

.010(.010)

.008(.008)

Hardness, Rock well

ASTM D785

R90

R90

R80

R90

R85

R80

R82

R82

Reinforcement content %

ASTM D2584

12

20

12

25

40

20

25

35

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

1.1

(58.7)

1.0

(53.4)

1.5

(80.1)

1.4

(75.7)

1.3

(69.4)

1.6

(85.4)

1.5

(80.1)

1.5

(80.1)

Tensile strength

ASTM D638

4,000

(27.6)

4,000

(27.6)

3,500

(24.1)

3,900

(26.9)

3,600

(24.8)

3,800

(26.2)

3,400

(23.4)

3,400

(23.4)

Elongation, Ultimate %

ASTM D638

15

12

15

10

5

15

12

12

Flexural modulus

psi (MPa)

ASTM D790

260,000

(1793)

290,000

(2000)

240,000

(1655)

275,000

(1897)

420,000

(2897)

250,000

(1724)

270,000

(1862)

240,000

(1655)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

220(104)

153(67)

225(107)

155(68)

200(93)

150(66)

220(104)

170(77)

270(132)

180(82)

240(116)

150(65)

270(132)

160(71)

255(124)

180(82)

Special Features

Warp resistance improved impact resistance

Warp resistance improved impact resistance

Warp resistance improved impact resistance

Warp resistance improved impact resistance

Warp resistance improved impact resistance

Warp resistance improved impact resistance

Warp resistance improved impact resistance

Warp resistance improved impact resistance

Copolymer PP Combination filled details

PropertyDescription

V515R34

34% Glass/Mineral Reinforced

V515R35

35% Glass/Mineral Reinforced

Copolymer PP Combination test results

Property

Test Method

V515R34

V515R35

Description

34% Glass/Mineral reinforced

35% Glass/Mineral reinforced

Processing Method

Injection

Injection

Specific gravity, g/cc

ASTM D792

1.19

1.18

Linear mold shrinkage, in/in(m)

ASTM D955

.004(.004)

.004(.004)

Hardness, Rock well

ASTM D785

R90

R85

Reinforcement content %

ASTM D2584

34

35

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

1.0

(53.4)

1.2

(64.1)

Tensile strength

ASTM D638

8,700

(60.0)

6,500

(44.8)

Elongation, Ultimate %

ASTM D638

3

4

Flexural modulus

psi (MPa)

ASTM D790

800,000

(5517)

550,000

(3793)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

290(143)

260(127)

295(146)

270(132)

Special Features

Excellent stiffness &

Dimensional stability

Good balance of properties and warp resistance

Copolymer PP Talc filled details

Property Description

V515TL20

20% Talc Reinforced

V515TL40

40% Talc Reinforced

V525TL10

10% Talc Reinforced

V525TL20

20% Talc Reinforced

V525TL30

30% Talc Reinforced

V525TL40

40% Talc Reinforced

Copolymer PP Talc test results

Property

Test Method

V515TL20

V515TL40

V525TL10

V525TL20

V525TL30

V525TL40

Description

20% Talc reinforced

40% Talc reinforced

10% Talc reinforced

20% Talc reinforced

30% Talc reinforced

40% Talc reinforced

Processing Method

Injection

Injection

Injection

Injection

Injection

Injection

Specific gravity, g/cc

ASTM D792

1.05

1.24

0.98

1.05

1.13

1.24

Linear mold shrinkage, in/in(m)

ASTM D955

.011(.011)

.009(.009)

.012(.012)

.011(.011)

.010(.010)

.009(.009)

Hardness, Rock well

ASTM D785

R85

R90

R75

R85

R85

R90

Reinforcement content %

ASTM D2584

20

40

10

20

30

40

Notched izod impact,

 ft-lb/in(J/m)

ASTM D256

1.2

(64.1)

1.2

(64.1)

1.5

(80.1)

1.4

(74.7)

1.7

(90.8)

1.5

(80.1)

Tensile strength

ASTM D638

3,900

(26.9)

3,800

(26.2)

3,900

(26.9)

3,700

(25.5)

3,600

(24.8)

3,500

(24.1)

Elongation, Ultimate %

ASTM D638

12

10

25

15

15

12

Flexural modulus

psi (MPa)

ASTM D790

290,000

(2000)

350,000

(2414)

230,000

(1586)

280,000

(1931)

280,000

(1931)

320,000

(2207)

Heat detection temp,

@66 psi °F(°C)

@264 psi °F(°C)

ASTM D648

230(110)

180(82)

270(132)

180(82)

210(99)

155(68)

215(102)

160(71)

215(102)

160(71)

225(107)

170(77)

Special Features

Good dimensional stability UL9HB

Impact modified

Good impact resistance

Good impact resistance

Good impact resistance

Good impact resistance